| Standard |
Material Designation |
Chemical Composition (%) |
| GB /T 20878-2007 | 022Cr19Ni10
(S30403)
(00Cr19Ni10)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
| Min |
- |
- |
- |
- |
- |
8 |
18 |
| Max |
0.03 |
1 |
2 |
0.045 |
0.03 |
12 |
20 |
|
JIS G 4303-2005
Stainless steel bars | SUS304L
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
| Min |
- |
- |
- |
- |
- |
9 |
18 |
| Max |
0.03 |
1 |
2 |
0.045 |
0.03 |
13 |
20 |
|
ASTM A 959-2004
Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels | 304L
(S30403)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
| Min |
- |
- |
- |
- |
- |
8 |
18 |
| Max |
0.03 |
1 |
2 |
0.045 |
0.03 |
12 |
20 |
|
EN 10088-1-2005
Staehle Stainless steels. Part 1:List of stainless steels | X2CrNi19-11
(1.4306)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
N |
| Min |
- |
- |
- |
- |
- |
10 |
18 |
- |
| Max |
0.03 |
1 |
2 |
0.045 |
0.015 |
12 |
20 |
0.11 |
|
EN 10296-2-2005
Welded circular steel tubes for mechanical and general engineering purposes — Technical delivery conditions — Part 2 Stainless steel | 1.4306
(X2CrNi19-11)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
N |
| Min |
- |
- |
- |
- |
- |
10 |
18 |
- |
| Max |
0.03 |
1 |
2 |
0.045 |
0.015 |
12 |
20 |
0.11 |
|
EN 10253-4-2003
Butt-welding pipe fittings. Wrought austenitic and austenitic-ferritic (duplex) stainless steels with specific inspection requirements | 1.4306
(X2CrNi19-11)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
N |
| Min |
- |
- |
- |
- |
- |
10 |
18 |
- |
| Max |
0.03 |
1 |
2 |
0.045 |
0.015 |
12 |
20 |
0.11 |
|
EN 10263-5-2001
teel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels | 1.4306
(X2CrNi19-11)
|
|
C |
Si |
Mn |
P |
S |
Cu |
Ni |
Cr |
N |
| Min |
- |
- |
- |
- |
- |
- |
10 |
18 |
- |
| Max |
0.03 |
1 |
2 |
0.045 |
0.03 |
1 |
12 |
20 |
0.11 |
|
| EN 10250-4-1999 | 1.4306
(X2CrNi19-11)
|
|
C |
Si |
Mn |
P |
S |
Ni |
Cr |
N |
| Min |
- |
- |
- |
- |
- |
10 |
18 |
- |
| Max |
0.03 |
1 |
2 |
0.045 |
0.03 |
12 |
20 |
0.11 |
|