EN 10302-2008
Material Designation Chemical Composition (%)
1.4903 (X10CrMoVNb9-1)
C Si Mn P S Ni Cr N Al Mo V Nb
Min 0.08 - 0.3 - - - 8 0.03 - 0.85 0.18 0.06
Max 0.12 0.5 0.6 0.025 0.015 0.4 9.5 0.07 0.03 1.05 0.25 0.1
1.4905 (X11CrMoWVNb9-1-1)
C Si Mn P S Ni Cr N B Al Mo W V Nb
Min 0.09 0.1 0.3 - - 0.1 8.5 0.05 0.0005 - 0.9 0.9 0.18 0.06
Max 0.13 0.5 0.6 0.02 0.01 0.4 9.5 0.09 0.005 0.04 1.1 1.1 0.25 0.1
1.4911 (X8CrCoNiMo10-6)
C Si Mn P S Ni Cr N B Mo W V Nb Co
Min 0.05 0.1 0.3 - - 0.2 9.8 - 0.005 0.5 - 0.1 0.2 5
Max 0.12 0.8 1.3 0.025 0.015 1.2 11.2 0.035 0.015 1 0.7 0.4 0.5 7
1.4913 (X19CrMoNbVN11-1)
C Si Mn P S Ni Cr N B Al Mo V Nb
Min 0.17 - 0.4 - - 0.2 10 0.05 - - 0.5 0.1 0.25
Max 0.23 0.5 0.9 0.025 0.015 0.6 11.5 0.1 0.0015 0.02 0.8 0.3 0.55
1.4922 (X20CrMoV11-1)
C Si Mn P S Ni Cr Mo V
Min 0.17 - - - - 0.3 10 0.8 0.25
Max 0.23 0.5 1 0.025 0.015 0.8 12.5 1.2 0.35
1.4923 (X22CrMoV12-1)
C Si Mn P S Ni Cr Mo V
Min 0.18 - 0.4 - - 0.3 11 0.8 0.25
Max 0.24 0.5 0.9 0.025 0.015 0.8 12.5 1.2 0.35
1.4935 (X20CrMoWV12-1)
C Si Mn P S Ni Cr Mo W V
Min 0.17 0.1 0.3 - - 0.3 11 0.8 0.4 0.2
Max 0.24 0.5 0.8 0.025 0.015 0.8 12.5 1.2 0.6 0.35
1.4938 (X12CrNiMoV12-3)
C Si Mn P S Ni Cr N Mo V
Min 0.08 - 0.4 - - 2 11 0.02 1.5 0.25
Max 0.15 0.5 0.9 0.025 0.015 3 12.5 0.04 2 0.4
1.4910 (X3CrNiMoBN17-13-3)
C Si Mn P S Ni Cr N B Mo
Min - - - - - 12 16 0.1 0.0015 2
Max 0.04 0.75 2 0.035 0.015 14 18 0.18 0.005 3
1.4919 (X6CrNiMoB17-12-2)
C Si Mn P S Ni Cr N B Mo
Min 0.04 - - - - 10 16.5 - 0.0015 2
Max 0.08 1 2 0.035 0.015 13 18.5 0.1 0.005 2.5
1.4941 (X6CrNiTiB18-10)
C Si Mn P S Ni Cr B Ti
Min 0.04 - - - - 9 17 0.0015 -
Max 0.08 1 2 0.035 0.015 12 19 0.005 0.8
1.4945 (X6CrNiWNbN16-16)
C Si Mn P S Ni Cr N W Nb
Min 0.04 0.3 - - - 15.5 15.5 0.06 2.5 -
Max 0.1 0.6 1.5 0.035 0.015 17.5 17.5 0.14 3.5 1.2
1.4951 (X6CrNi25-20)
C Si Mn P S Ni Cr N
Min 0.04 - - - - 19 24 -
Max 0.08 0.7 2 0.035 0.015 22 26 0.1
1.4958 (X5NiCrAlTi31-20)
C Si Mn P S Cu Ni Cr Al Ti Nb
Min 0.03 - - - - - 30 19 0.2 0.2 -
Max 0.08 0.7 1.5 0.015 0.01 0.5 32.5 22 0.5 0.5 0.1
1.4959 (X8NiCrAlTi32-21)
C Si Mn P S Cu Ni Cr Al Ti
Min 0.05 - - - - - 30 19 0.25 0.25
Max 0.1 0.7 1.5 0.015 0.01 0.5 34 22 0.65 0.65
1.4961 (X8CrNiNb16-13)
C Si Mn P S Ni Cr Nb
Min 0.04 0.3 - - - 12 15 -
Max 0.1 0.6 1.5 0.035 0.015 14 17 1.2
1.4962 (X12CrNiWTiB16-13)
C Si Mn P S Ni Cr B W Ti
Min 0.07 - - - - 12.5 15.5 0.0015 2.5 0.4
Max 0.15 0.5 1.5 0.035 0.015 14.5 17.5 0.006 3 0.7
1.4971 (X12CrCoNi21-20)
C Si Mn P S Ni Cr N Mo W Nb Co
Min 0.08 - - - - 19 20 0.1 2.5 2 0.75 18.5
Max 0.16 1 2 0.035 0.015 21 22.5 0.2 3.5 3 1.25 21
1.4980 (X6NiCrTiMoVB25-15-2)
C Si Mn P S Ni Cr B Al Mo Ti V
Min 0.03 - 1 - - 24 13.5 0.003 - 1 1.9 0.1
Max 0.08 1 2 0.025 0.015 27 16 0.01 0.35 1.5 2.3 0.5
1.4981 (X8CrNiMoNb16-16)
C Si Mn P S Ni Cr Mo Nb
Min 0.04 0.3 - - - 15.5 15.5 1.6 -
Max 0.1 0.6 1.5 0.035 0.015 17.5 17.5 2 1.2
1.4983 (X6CrNiMoTiB17-13)
C Si Mn P S Ni Cr B Mo Ti
Min 0.04 - - - - 12 16 0.0015 2 -
Max 0.08 0.75 2 0.035 0.015 14 18 0.006 2.5 0.8
1.4988 (X8CrNiMoVNb16-13)
C Si Mn P S Ni Cr N Mo V Nb
Min 0.04 0.3 - - - 12.5 15.5 0.06 1.1 0.6 -
Max 0.1 0.6 1.5 0.035 0.015 14.5 17.5 0.14 1.5 0.85 1.2
2.4608 (NiCr26MoW)
Fe C Si Mn P S Ni Cr Mo W Co
Min 11.375 0.03 0.7 - - - 44 24 2.5 2.5 2.5
Max 23.77 0.08 1.5 2 0.03 0.015 47 26 4 4 4
2.4632 (NiCr20Co18Ti)
Fe C Si Mn P S Cu Ni Cr B Al Ti Zr Co
Min - - - - - - - 48.965 18 - 1 2 - 15
Max 1.5 0.13 1 1 0.02 0.015 0.2 64 21 0.02 2 3 0.15 21
2.4633 (NiCr25FeAlY)
Fe C Si Mn P S Cu Ni Cr Al Ti Zr
Min 8 0.15 - - - - - 58.8 24 1.8 0.1 0.01
Max 11 0.25 0.5 0.5 0.02 0.01 0.1 65.89 26 2.4 0.2 0.1
2.4642 (NiCr29Fe)
Fe C Si Mn P S Cu Ni Cr Al
Min 7 - - - - - - 55.915 27 -
Max 11 0.05 0.5 0.5 0.02 0.015 0.5 66 31 0.5
2.4650
Fe C Si Mn P S Cu Cr B Al Mo Ti Co
Min - 0.04 - - - - - 19 - 0.3 5.6 1.9 19
Max 0.7 0.08 0.4 0.6 0.02 0.007 0.2 21 0.005 0.6 6.1 2.4 21
2.4654 (NiCr20Co13Mo4Ti3Al)
Fe C Si Mn P S Cu Ni Cr B Al Mo Ti Zr Co
Min - 0.02 - - - - - 50.63 18 0.003 1.2 3.5 2.8 0.02 12
Max 2 0.1 0.15 1 0.015 0.015 0.1 62.457 21 0.01 1.6 5 3.3 0.08 15
2.4663 (NiCr23Co12Mo)
Fe C Si Mn P S Cu Ni Cr B Al Mo Ti Co
Min - 0.05 - - - - - 47.974 20 - 0.7 8.5 0.2 11
Max 2 0.1 0.2 0.2 0.01 0.01 0.5 59.55 23 0.006 1.4 10 0.6 14
2.4665 (NiCr22Fe18Mo)
Fe C Si Mn P S Cu Ni Cr B Al Mo W Co
Min 17 0.05 - - - - - 40.305 20.5 - - 8 0.2 0.5
Max 20 0.15 1 1 0.02 0.015 0.5 53.75 23 0.01 0.5 10 1 2.5
2.4668 (NiCr18Fe19Nb5Mo3)
Fe C Si Mn P S Cu Ni Cr B Al Mo Ti Co
Min 12.184 0.02 - - - - - 50 17 0.002 0.3 2.8 0.6 -
Max 24.578 0.08 0.35 0.35 0.015 0.015 0.3 55 21 0.006 0.7 3.3 1.2 1
2.4669 (NiCr15Fe7TiAl)
Fe C Si Mn P S Cu Cr Al Ti Co
Min 5 - - - - - - 14 0.4 2.25 -
Max 9 0.08 0.5 1 0.02 0.015 0.5 17 1 2.75 1
2.4952 (NiCr20TiAl)
Fe C Si Mn P S Cu Cr B Al Ti Co
Min - 0.04 - - - - - 18 - 1 1.8 -
Max 1.5 0.1 1 1 0.02 0.015 0.2 21 0.008 1.8 2.7 1
2.4878 (NiCr25Co20TiMo)
Fe C Si Mn P S Cu Ni Cr B Al Mo Ti Zr Co
Min - 0.03 - - - - - 43.578 23 0.01 1.2 1 2.8 0.03 19
Max 1 0.07 0.5 0.5 0.01 0.007 0.2 52.23 25 0.015 1.6 2 3.2 0.07 21
2.4964 (CoCr20W15Ni)
Fe C Si Mn P S Ni Cr W Co
Min - 0.05 - - - - 9 19 14 46.415
Max 3 0.15 0.4 2 0.02 0.015 11 21 16 57.95