EN 10263-5-2001
teel rod, bars and wire for cold heading and cold extrusion - Part 5: Technical delivery conditions for stainless steels
Material Designation Chemical Composition (%)
1.4016 (X6Cr17)
C Si Mn P S Cr
Min - - - - - 16
Max 0.08 1 1 0.04 0.03 18
1.4113 (X6CrMo17-1)
C Si Mn P S Cr Mo
Min - - - - - 16 0.9
Max 0.08 1 1 0.04 0.03 18 1.4
1.4006 (X12Cr13)
C Si Mn P S Ni Cr
Min 0.08 - - - - - 11.5
Max 0.15 1 1.5 0.04 0.03 0.75 13.5
1.4462 (X2CrNiMoN22-5-3)
C Si Mn P S Ni Cr N Mo
Min - - - - - 4.5 21 0.1 2.5
Max 0.03 1 2 0.035 0.015 6.5 23 0.22 3.5
1.4310 (X10CrNi18-8)
C Si Mn P S Cu Ni Cr N Mo
Min 0.05 - - - - - 6 16 - -
Max 0.15 2 2 0.045 0.015 1 9 19 0.11 0.8
1.4307 (X2CrNi18-9)
C Si Mn P S Cu Ni Cr N
Min - - - - - - 8 17.5 -
Max 0.03 1 2 0.045 0.03 1 10 19.5 0.11
1.4306 (X2CrNi19-11)
C Si Mn P S Cu Ni Cr N
Min - - - - - - 10 18 -
Max 0.03 1 2 0.045 0.03 1 12 20 0.11
1.4301 (X5CrNi18-10)
C Si Mn P S Cu Ni Cr N
Min - - - - - - 8 17 -
Max 0.07 1 2 0.045 0.03 1 10.5 19.5 0.11
1.4541 (X6CrNiTi18-10)
C Si Mn P S Cu Ni Cr Ti
Min - - - - - - 9 17 -
Max 0.08 1 2 0.045 0.03 1 12 19 0.7
1.4303 (X4CrNi18-12)
C Si Mn P S Ni Cr N
Min - - - - - 11 17 -
Max 0.06 1 2 0.045 0.03 13 19 0.11
1.4404 (X2CrNiMo17-12-2)
C Si Mn P S Cu Ni Cr N Mo
Min - - - - - - 10 16.5 - 2
Max 0.03 1 2 0.045 0.03 1 13 18.5 0.11 2.5
1.4432 (X2CrNiMo17-12-3)
C Si Mn P S Cu Ni Cr N Mo
Min - - - - - - 10.5 16.5 - 2.5
Max 0.03 1 2 0.045 0.015 1 13 18.5 0.11 3
1.4401 (X5CrNiMo17-12-2)
C Si Mn P S Cu Ni Cr N Mo
Min - - - - - - 10 16.5 - 2
Max 0.07 1 2 0.045 0.03 1 13 18.5 0.11 2.5
1.4571 (X6CrNiMoTi17-12-2)
C Si Mn P S Cu Ni Cr Mo Ti
Min - - - - - - 10.5 16.5 2 -
Max 0.08 1 2 0.045 0.03 1 13.5 18.5 2.5 0.7
1.4429 (X2CrNiMoN17-13-3)
C Si Mn P S Cu Ni Cr N Mo
Min - - - - - - 11 16.5 0.12 2.5
Max 0.03 1 2 0.045 0.015 1 14 18.5 0.22 3
1.4436 (X3CrNiMO17-13-3)
C Si Mn P S Ni Cr N Mo
Min - - - - - 10.5 16.5 - 2.5
Max 0.05 1 2 0.045 0.015 13 18.5 0.11 3
1.4567 (X3CrNiCu18-9-4)
C Si Mn P S Cu Ni Cr N
Min - - - - - 3 8.5 17 -
Max 0.04 1 2 0.045 0.03 4 10.5 19 0.11
1.4560 (X3CrNiCu19-9-2)
C Si Mn P S Cu Ni Cr N
Min - - 1.5 - - 1.5 8 18 -
Max 0.035 1 2 0.045 0.015 2 9 19 0.11
1.4578 (X3CrNiCuMo17-11-3-2)
C Si Mn P S Cu Ni Cr N Mo
Min - - - - - 3 10 16.5 - 2
Max 0.04 1 1 0.045 0.015 3.5 11 17.5 0.11 2.5