EN 10268-2006
cold rolled steel flat products with high yield strength for cold forming - technical delivery conditions
Material Designation Chemical Composition (%)
1.0922 (HC180Y)
C Si Mn P S Ti
Min - - - - - -
Max 0.01 0.3 0.7 0.06 0.025 0.12
1.0342 (HC180P)
C Si Mn P S
Min - - - - -
Max 0.05 0.4 0.6 0.08 0.025
1.0395 (HC180B)
C Si Mn P S
Min - - - - -
Max 0.05 0.5 0.7 0.06 0.025
1.0925 (HC220Y)
C Si Mn P S Ti
Min - - - - - -
Max 0.01 0.3 0.9 0.08 0.025 0.12
1.0346 (HC220I)
C Si Mn P S Ti
Min - - - - - -
Max 0.07 0.5 0.5 0.05 0.025 0.05
1.0397 (HC220P)
C Si Mn P S
Min - - - - -
Max 0.07 0.5 0.7 0.08 0.025
1.0396 (HC220B)
C Si Mn P S
Min - - - - -
Max 0.06 0.5 0.7 0.08 0.025
1.0928 (HC260Y)
C Si Mn P S Ti
Min - - - - - -
Max 0.01 0.3 1.6 0.1 0.025 0.12
1.0349 (HC260I)
C Si Mn P S Ti
Min - - - - - -
Max 0.07 0.5 0.5 0.05 0.025 0.05
1.0417 (HC260P)
C Si Mn P S
Min - - - - -
Max 0.08 0.5 0.7 0.1 0.025
1.0400 (HC260B)
C Si Mn P S
Min - - - - -
Max 0.08 0.5 0.7 0.1 0.025
1.0480 (HC260LA)
C Si Mn P S Ti
Min - - - - - -
Max 0.1 0.5 0.6 0.025 0.025 0.15
1.0447 (HC300I)
C Si Mn P S Ti
Min - - - - - -
Max 0.08 0.5 0.7 0.08 0.025 0.05
1.0448 (HC300P)
C Si Mn P S
Min - - - - -
Max 0.1 0.5 0.7 0.12 0.025
1.0444 (HC300B)
C Si Mn P S
Min - - - - -
Max 0.1 0.5 0.7 0.12 0.025
1.0489 (HC300LA)
C Si Mn P S Ti Nb
Min - - - - - - -
Max 0.1 0.5 1 0.025 0.025 0.15 0.09
1.0548 (HC340LA)
C Si Mn P S Ti Nb
Min - - - - - - -
Max 0.1 0.5 1.1 0.025 0.025 0.15 0.09
1.0050 (HC380LA)
C Si Mn P S Ti Nb
Min - - - - - - -
Max 0.1 0.5 1.6 0.025 0.025 0.15 0.09
1.0556 (HC420LA)
C Si Mn P S Ti Nb
Min - - - - - - -
Max 0.1 0.5 1.6 0.025 0.025 0.15 0.09
For Reference Only