EN 13835-2002
Material Designation Chemical Composition (%)
JL3011 (GJLA-XNiCuCr15-6-2)
C Si Mn P Cu Ni Cr
Min - 1 0.5 - 5.5 13.5 1
Max 3 2.8 1.5 0.25 7.5 17.5 3.5
JS3011 (GJSA-XNiCr20-2)
C Si Mn P Cu Ni Cr
Min - 1.5 0.5 - - 18 1
Max 3 3 1.5 0.08 0.5 22 3.5
JS3021 (GJSA-XNiMn23-4)
C Si Mn P Cu Ni Cr
Min - 1.5 4 - - 22 -
Max 2.6 2.5 4.5 0.08 0.5 24 0.2
JS3031 (GJSA-XNiCrNb20-2)
C Si Mn P Cu Ni Cr Nb
Min - 1.5 0.5 - - 18 1 0.12
Max 3 2.4 1.5 0.08 0.5 22 3.5 0.2
JS3041 (GJSA-XNi22)
C Si Mn P Cu Ni Cr
Min - 1 1.5 - - 21 -
Max 3 3 2.5 0.08 0.5 24 0.5
JS3051 (GJSA-XNi35)
C Si Mn P Cu Ni Cr
Min - 1.5 0.5 - - 34 -
Max 2.4 3 1.5 0.08 0.5 36 0.2
JS3061 (GJSA-XNiSiCr35-5-2)
C Si Mn P Cu Ni Cr
Min - 4 0.5 - - 34 1.5
Max 2 6 1.5 0.08 0.5 36 2.5
JL3021 (GJSA-XNiMn13-7)
C Si Mn P Cu Ni Cr
Min - 1.5 6 - - 12 -
Max 3 3 7 0.25 0.5 14 0.2
JS3071 (GJSA-XNiMn13-7)
C Si Mn P Cu Ni Cr
Min - 2 6 - - 12 -
Max 3 3 7 0.08 0.5 14 0.2
JS3081 (GJSA-XNiCr30-3)
C Si Mn P Cu Ni Cr
Min - 1.5 0.5 - - 28 2.5
Max 2.6 3 1.5 0.08 0.5 32 3.5
JS3091 (GJSA-XNiSiCr30-5-5)
C Si Mn P Cu Ni Cr
Min - 5 0.5 - - 28 4.5
Max 2.6 6 1.5 0.08 0.5 32 5.5
JS3101 (GJSA-XNiCr35-3)
C Si Mn P Cu Ni Cr
Min - 1.5 0.5 - - 34 2
Max 2.4 3 1.5 0.08 0.5 36 3
For Reference Only