EN 10263-3-2001
Steel rod,bars and wire for cold heading and cold extrusion - Part 3: Technical delivery conditions for case hardening steels
Material Designation Chemical Composition (%)
1.1152 (C20E2C)
C Si Mn P S Cu
Min 0.18 - 0.3 - - -
Max 0.22 0.3 0.6 0.025 0.025 0.25
1.5503 (18B2)
C Si Mn P S Cu B
Min 0.16 - 0.6 - - - 0.0008
Max 0.2 0.3 0.8 0.025 0.025 0.25 0.005
1.1122 (C10E2C)
C Si Mn P S Cu
Min 0.08 - 0.3 - - -
Max 0.12 0.3 0.6 0.025 0.025 0.25
1.1132 (C15E2C)
C Si Mn P S Cu
Min 0.13 - 0.3 - - -
Max 0.17 0.3 0.6 0.025 0.025 0.25
1.1147 (C17E2C)
C Si Mn P S Cu
Min 0.15 - 0.6 - - -
Max 0.19 0.3 0.9 0.025 0.025 0.25
1.5501 (15B2)
C Si Mn P S Cu B
Min 0.13 - 0.6 - - - 0.0008
Max 0.16 0.3 0.8 0.025 0.025 0.25 0.005
1.5521 (18MnB4)
C Si Mn P S Cu B
Min 0.16 - 0.9 - - - 0.0008
Max 0.2 0.3 1.2 0.025 0.025 0.25 0.005
1.5522 (22MnB4)
C Si Mn P S Cu B
Min 0.2 - 0.9 - - - 0.0008
Max 0.24 0.3 1.2 0.025 0.025 0.25 0.005
1.7016 (17Cr3)
C Si Mn P S Cu Cr
Min 0.14 - 0.6 - - - 0.7
Max 0.2 0.3 0.9 0.025 0.025 0.25 1
1.7014 (17CrS3)
C Si Mn P S Cu Cr
Min 0.14 - 0.6 - 0.02 - 0.7
Max 0.2 0.3 0.9 0.025 0.04 0.25 1
1.7131 (16MnCr5)
C Si Mn P S Cu Cr
Min 0.14 - 1 - - - 0.8
Max 0.19 0.3 1.3 0.025 0.025 0.25 1.1
1.7139 (16MnCrS5)
C Si Mn P S Cu Cr
Min 0.14 - 1 - 0.02 - 0.8
Max 0.19 0.3 1.3 0.025 0.04 0.25 1.1
1.7160 (16MnCrB5)
C Si Mn P S Cu Cr B
Min 0.14 - 1 - - - 0.8 0.0008
Max 0.19 0.3 1.3 0.025 0.025 0.25 1.1 0.005
1.7149 (20MnCrS5)
C Si Mn P S Cu Cr
Min 0.17 - 1.1 - 0.02 - 1
Max 0.22 0.3 1.4 0.025 0.04 0.25 1.3
1.7201 (12CrMo4)
C Si Mn P S Cu Cr Mo
Min 0.1 - 0.6 - - - 0.9 0.15
Max 0.15 0.3 0.9 0.025 0.025 0.25 1.2 0.25
1.7243 (18CrMo4)
C Si Mn P S Cu Cr Mo
Min 0.15 - 0.6 - - - 0.9 0.15
Max 0.21 0.3 0.9 0.025 0.025 0.25 1.2 0.25
1.7244 (18CrMoS4)
C Si Mn P S Cu Cr Mo
Min 0.15 - 0.6 - 0.02 - 0.9 0.15
Max 0.21 0.3 0.9 0.025 0.04 0.25 1.2 0.25
1.7321 (20MoCr4)
C Si Mn P S Cu Cr Mo
Min 0.17 - 0.7 - - - 0.3 0.4
Max 0.23 0.3 1 0.025 0.025 0.25 0.6 0.5
1.7323 (20MoCrS4)
C Si Mn P S Cu Cr Mo
Min 0.17 - 0.7 - 0.02 - 0.3 0.4
Max 0.23 0.3 1 0.025 0.04 0.25 0.6 0.5
1.5805 (10NiCr5-4)
C Si Mn P S Cu Ni Cr
Min 0.07 - 0.6 - - - 1.2 0.9
Max 0.12 0.3 0.9 0.025 0.025 0.25 1.5 1.2
1.5701 (12NiCr3-2)
C Si Mn P S Cu Ni Cr
Min 0.09 - 0.3 - - - 0.5 0.4
Max 0.15 0.3 0.6 0.025 0.025 0.25 0.8 0.7
1.5918 (17CrNi6-6)
C Si Mn P S Cu Ni Cr
Min 0.14 - 0.5 - - - 1.4 1.4
Max 0.2 0.3 0.9 0.025 0.025 0.25 1.7 1.7
1.6523 (20NiCrMo2-2)
C Si Mn P S Cu Ni Cr Mo
Min 0.17 - 0.65 - - - 0.4 0.35 0.15
Max 0.23 0.3 0.95 0.025 0.025 0.25 0.7 0.7 0.25
1.6526 (20NiCrMoS2-2)
C Si Mn P S Cu Ni Cr Mo
Min 0.17 - 0.65 - 0.02 - 0.4 0.35 0.15
Max 0.23 0.3 0.95 0.025 0.04 0.25 0.7 0.7 0.25
1.6571 (20NiCrMoS6-4)
C Si Mn P S Cu Ni Cr Mo
Min 0.16 - 0.5 - 0.02 - 1.4 0.6 0.25
Max 0.23 0.3 0.9 0.025 0.04 0.25 1.7 0.9 0.35
For Reference Only