EN 10263-2-2001
Steel rod,bars and wire for cold heading and cold extrusion - Part 2: Technical delivery conditions for steels not intended for heat treatment after cold working
Material Designation Chemical Composition (%)
C4C (1.0303)
C Si Mn P S Al
Min 0.02 - 0.25 - - 0.02
Max 0.06 0.1 0.4 0.02 0.025 0.06
C8C (1.0213)
C Si Mn P S Al
Min 0.06 - 0.25 - - 0.02
Max 0.1 0.1 0.45 0.02 0.025 0.06
C10C (1.0214)
C Si Mn P S Al
Min 0.08 - 0.3 - - 0.02
Max 0.12 0.1 0.5 0.025 0.025 0.06
C15C (1.0234)
C Si Mn P S Al
Min 0.13 - 0.35 - - 0.02
Max 0.17 0.1 0.6 0.025 0.025 0.06
C15E2C (1.1132)
C Si Mn P S Cu
Min 0.13 - 0.3 - - -
Max 0.17 0.03 0.6 0.025 0.025 0.25
C20C (1.0411)
C Si Mn P S Al
Min 0.18 - 0.7 - - 0.02
Max 0.22 0.1 0.9 0.025 0.025 0.06
C20E2C (1.1152)
C Si Mn P S Cu
Min 0.18 - 0.3 - - -
Max 0.22 0.3 0.6 0.025 0.025 0.25
C17C (1.0434)
C Si Mn P S Al
Min 0.15 - 0.65 - - 0.02
Max 0.19 0.1 0.85 0.025 0.025 0.06
17Cr3 (1.7016)
C Si Mn P S Cu Cr
Min 0.14 - 0.6 - - - 0.7
Max 0.2 0.3 0.9 0.025 0.025 0.25 1
C2C (1.0314)
C Si Mn P S Al
Min - - 0.2 - - 0.02
Max 0.03 0.1 0.4 0.02 0.025 0.06
8MnSi7 (1.5113)
C Si Mn P S Al
Min - 0.9 1.6 - - 0.02
Max 0.1 1.1 1.8 0.025 0.025 0.06