C10
Standard ISO 683-18-1996 Heat-treatable steels, alloy steels and free-cutting steels
Standard DIN 17210-1986 Case hardening steel coil
Standard EN 10277-2-2008 Bright steel products - Technical delivery conditions - Part 2: Steels for general engineering purposes
Standard Material Designation Chemical Composition (%)
ISO 683-18-1996
Heat-treatable steels, alloy steels and free-cutting steels
08F
(U 20080)
C Si Mn P S Cu Ni Cr
Min 0.05 - 0.25 - - - - -
Max 0.11 0.3 0.5 0.035 0.035 0.25 0.3 0.1
ISO 683-18-1996
Heat-treatable steels, alloy steels and free-cutting steels
C10
C Si Mn P S
Min 0.07 0.1 0.3 - -
Max 0.13 0.35 0.6 0.035 0.035
ISO 683-18-1996
Heat-treatable steels, alloy steels and free-cutting steels
S09CK
C Si Mn P S Cu Ni Cr
Min 0.07 0.1 0.3 - - - - -
Max 0.12 0.35 0.6 0.025 0.025 0.25 0.2 0.2
KS D 3752-2007 S9CK
C Si Mn P S Cu Ni Cr
Min 0.07 0.1 0.3 - - - - -
Max 0.12 0.35 0.6 0.025 0.025 0.25 0.2 0.2
DIN 17210-1986
Case hardening steel coil
C10
(1.0301)
C Si Mn P S
Min 0.07 - 0.3 - -
Max 0.13 0.4 0.6 0.045 0.045
ASTM A29M UNS-2012
Standard Specification for General Requirements for Steel Bars, Carbon and Alloy, Hot-Wrought
1008
(G10080)
C Si Mn P S Cu
Min - - 0.3 - - -
Max 0.1 0.1 0.5 0.04 0.05 0.2
EN 10277-2-2008
Bright steel products - Technical delivery conditions - Part 2: Steels for general engineering purposes
1.0301
(C10)
C Si Mn P S
Min 0.07 - 0.3 - -
Max 0.13 0.4 0.6 0.045 0.045
Cross Reference Table
GB
08F
-
U 20080
ISO
C10
JIS
S09CK
KS
S9CK
DIN
1.0301
ASTM
1008
ASTM
G10080
For Reference Only